Title: Size-dependent magnetic parameters of fcc FePt nanoparticles: applications to magnetic hyperthermia
Authors: 國立臺灣師範大學化學系
M. S. Seehra
V. Singh
P. Dutta
S. Neeleshwar
Y.-Y. Chen
C.-L. Chen
S.-W. Chou
Chia-Chun Chen
Issue Date: 14-Apr-2010
Publisher: IOP Publishing
Abstract: For nominal 3 and 9 nm FePt nanoparticles coated with oleylamine/oleic acid and having a face-centred-cubic (fcc) structure, temperature variations (5–300 K) of magnetization M, ac susceptibility χ' and χ'' for the frequency range fm = 0.1–1000 Hz and electron magnetic resonance (EMR) spectra at 9.28 GHz are reported. X-ray diffraction of the samples shows fcc structure with a lattice constant a = 3.84 Å and TEM characterization yields log-normal distributions of the particle sizes with average D = 3.15(0.16) nm and D = 8.70(0.12) nm for the 3 nm and 9 nm samples, respectively. M versus T data for the zero-field-cooled and field-cooled modes yield a blocking temperature TB = 15 K (85 K) for the 3 nm (9 nm) samples whereas the hysteresis loops at 5 K yield a coercivity Hc = 0 Oe (1.4 kOe). Analysis of the data of TB at different fm determined from the peaks in χ'' in ac susceptibility and the temperature variation of the EMR spectra are used to determine the following parameters of the Vogel–Fulcher relaxation for the 3 nm (9 nm) samples respectively: the attempt frequency fo = 8 × 1010 Hz (2 × 1012 Hz); inter-particle interaction temperature To = 3 K (33 K) and anisotropy Ka = 1.96 × 106 ergs cm−3 (4.3 × 105 ergs cm−3). The use of the above parameters for the calculations of the optimum size for magnetic hyperthermia is analysed and discussed.
ISSN: 0022-3727
Other Identifiers: ntnulib_tp_C0301_01_064
Appears in Collections:教師著作

Files in This Item:
There are no files associated with this item.

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.