標題: Growth Mechanism, Structure and IR Photoluminescence Studies of Indium Nitride Nanorods
作者: 國立臺灣師範大學化學系
Z.-H. Lan
W.-M. Wang
C.-L. Sun
S.-C. Shi
C.-W. Hsu
T.-T. Chen
K.-H. Chen
Chia-Chun Chen
Y.-F. Chen
L.-C. Chen
公開日期: 15-八月-2004
出版社: Elsevier
摘要: High-quality single crystal indium nitride nanorods were grown on Si substrates by catalytic chemical vapor deposition. Both Raman and high resolution transmission electron microscopic analyses suggested that even a minute amount of oxygen, from the residual oxygen in the growth environment and/or native oxide on the Si, would effectively help the growth of InN nanorods. The In2O3 formed on Au nanoparticles helped dissolve nitrogen as a catalyst with the subsequent growth of InN nanorods. Variations in the apparent color and photoluminescence (PL) spectra of the InN nanorods were observed. For the optically brown InN nanorods that exhibited diameters in the range of 30–50 nm, the PL study showed a peak at 1.9 eV, the possible origins of which are discussed. In contrast, for the optically black InN nanorods that exhibited diameters in the range of 50–100 nm, the PL peak at approximately 0.766 eV measured at 20 K was attributed to band edge emission.
URI: http://rportal.lib.ntnu.edu.tw/handle/20.500.12235/42313
ISSN: 0022-0248
其他識別: ntnulib_tp_C0301_01_029
顯示於類別:教師著作

文件中的檔案:
沒有與此文件相關的檔案。


在 DSpace 系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。