Titel: Growth Mechanism, Structure and IR Photoluminescence Studies of Indium Nitride Nanorods
Autoren: 國立臺灣師範大學化學系
Z.-H. Lan
W.-M. Wang
C.-L. Sun
S.-C. Shi
C.-W. Hsu
T.-T. Chen
K.-H. Chen
Chia-Chun Chen
Y.-F. Chen
L.-C. Chen
Erscheinungsdatum: 15-Aug-2004
Herausgeber: Elsevier
Zusammenfassung: High-quality single crystal indium nitride nanorods were grown on Si substrates by catalytic chemical vapor deposition. Both Raman and high resolution transmission electron microscopic analyses suggested that even a minute amount of oxygen, from the residual oxygen in the growth environment and/or native oxide on the Si, would effectively help the growth of InN nanorods. The In2O3 formed on Au nanoparticles helped dissolve nitrogen as a catalyst with the subsequent growth of InN nanorods. Variations in the apparent color and photoluminescence (PL) spectra of the InN nanorods were observed. For the optically brown InN nanorods that exhibited diameters in the range of 30–50 nm, the PL study showed a peak at 1.9 eV, the possible origins of which are discussed. In contrast, for the optically black InN nanorods that exhibited diameters in the range of 50–100 nm, the PL peak at approximately 0.766 eV measured at 20 K was attributed to band edge emission.
URI: http://rportal.lib.ntnu.edu.tw/handle/20.500.12235/42313
ISSN: 0022-0248
Sonstige Kennungen: ntnulib_tp_C0301_01_029
Enthalten in den Sammlungen:教師著作

Dateien zu dieser Ressource:
Es gibt keine Dateien zu dieser Ressource.


Alle Ressourcen in diesem Repository sind urheberrechtlich geschützt, soweit nicht anderweitig angezeigt.